عنوان انگلیسی Synthesis and Characterization of Colloidal Nanosilica via an Ultrasound Assisted Route Based on Alkali Leaching of Silica Fume
چکیده انگلیسی مقاله Colloidal nanosilica is currently being produced by various methods which are mainly high energy intensive and/or not environmentally friendly. It is therefore essential to develop new energy-efficient and environmentally friendly technologies. This paper introduces a new ultrasound assisted route based on alkali leaching of silica fume for synthesis of colloidal silica nanoparticles. The effects of sonication time on the particle size distribution of the colloidalnanosilica are studied via dynamic light scattering (DLS). The results show that the shape and size of nanoparticles are strongly depended on the ultrasonic time. DLS results show that average diameter of the produced colloidal nanosilicadecreases sharply from 337.10 nm to 93.27 nm during the first 5 minutes of sonication. Continued sonication up to 30 minutes, however, shows relatively slight decrease in average diameter of the colloidal nanosilica. Further, the produced colloidal nanosilica is characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffractometry (XRD) and Fourier transform infrared (FTIR) spectroscopy.
کلیدواژه‌های انگلیسی مقاله Nanoparticles,nanosilica,Colloid,Silica fume,ultrasound
نویسندگان مقاله v جعفری |
cement research center, school of chemical engineering, iran university of science and technology, tehran, i. r. iran
سازمان اصلی تایید شده: دانشگاه علم و صنعت ایران (Iran university of science and technology)

a اله وردی |
cement research center, school of chemical engineering, iran university of science and technology, tehran, i. r. iran
سازمان اصلی تایید شده: دانشگاه علم و صنعت ایران (Iran university of science and technology)

نشانی اینترنتی http://www.ijnnonline.net/article_9049_f59fcf95f1435c37611e27f0b7a3c24c.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات