عنوان انگلیسی Effect of Nano-TiO2 Particles on the Corrosion Behavior of Chromium-Based Coatings
چکیده انگلیسی مقاله Nanosized TiO2 particles were prepared by sol–gel method. The TiO2 particles were co-deposited with chromium using electrodeposition technique. In investigating of coating surfaces by scanning electron microscope (SEM), the results showed that the morphology of the coating surface was changed by adding TiO2 nanoparticles to the chromium coating. The corrosion behavior of the coatings was assessed by polarization technique in four media such as seawater, pipeline water, distilled water and 3.5% NaCl solution. The results showed that adding the TiO2 nanoparticles into chromium coating, caused a decrease in current and rate of corrosion, and so increased the period of conservation from cupric undercoat.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله m نوروزی فر |
department of chemistry, university of sistan amp;amp; baluchestan, zahedan, i. r. iran

m خراسانی مطلق | khorasani motlagh
department of chemistry, university of sistan amp;amp; baluchestan, zahedan, i. r. iran

z یاوری |
department of chemistry, university of sistan amp;amp; baluchestan, zahedan, i. r. iran

نشانی اینترنتی http://www.ijnnonline.net/article_3823_e55c15e228739a54ac5dc6137ffd26b1.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات