International Journal of Nanoscience and Nanotechnology (IJNN)، جلد ۹، شماره ۲، صفحات ۹۵-۱۰۰
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Structural and Optical Study of SnO Nanoparticles Synthesized Using Microwave–Assisted Hydrothermal Route
چکیده انگلیسی مقاله SnO nanoparticles were synthesized using microwave–assisted hydrothermal method. It was noticed that at 300 and 600 watt microwave power, SnO formed and remained in the tetragonal phase. At 900 watt, SnO2 started appearing and a mixture of SnO and SnO2 phases coexisted. The particle size varied from ~2 to ~13 nm at 300 to 900 watt radiation power. The UV-V absorption spectra showed the excitonic peaks of ~288, ~300 and ~315 nm corresponding to crystal sizes of ~2, ~6 and ~10 nm, respectively. For particles larger than 10 nm, no excitonic peak was observed. The appearance of these excitonic peaks could be attributed to the conversion of indirect band gap in bulk SnO to direct band gap in SnO nanoparticles. To verify this assumption, photoluminescence spectroscopy was carried out. The results showed a strong emission of 677 nm upon excitation at 336 nm wavelength, confirmed the assumption.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله p بروجردیان |
department of passive defense, malek ashtar university of technology, tehran, i. r. iran
سازمان اصلی تایید شده: دانشگاه صنعتی مالک اشتر (Malek ashtar university of technology)

نشانی اینترنتی http://www.ijnnonline.net/article_3824_709200c4ff736b549f99c68a70ca78c9.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات