عنوان انگلیسی Structure and Magnetic Properties of Oxide Nanoparticles of Fe-Co-Ni Synthesized by Co-Precipitation Method
چکیده انگلیسی مقاله Oxide nanoparticles of Fe-Co-Ni were prepared in six different compositions by co-precipitation method. The as-synthesized nanoparticles were characterized by X-Ray Diffraction (XRD), Field Emission Scanning Electron microscope (FESEM), Fourier Transform Infrared (FT-IR) and Vibrating Sample Magnetometer (VSM). It was found that the nanoparticles had mean crystalline size of 30-55 nm and spherical shape. Specific surface area of the nanoparticles was between 27.47x104 cm2/g to 141.4x104 cm2/g which had been calculated by X-Ray Diffraction data. The magnetic measurements of nanoparticles were done at room temperature and found that nanoparticles exhibit a ferromagnetic behavior with different values of saturation magnetization and coercivity.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله a قاسمی |
department of physics, faculty of science, university of sistan and baluchestan, zahedan, i. r. iran

علی محمد داورپناه | a m
department of physics, faculty of science, university of sistan and baluchestan, zahedan, i. r. iran

m قدیری |
chemical engineering department, urmia university of technology uut , urmia , i. r. iran
سازمان اصلی تایید شده: دانشگاه ارومیه (Urmia university)

نشانی اینترنتی http://www.ijnnonline.net/article_3893_7e66b1d93c36df2ed478d4f6b7640bc7.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات