عنوان انگلیسی The Effect of Impurity of Inert Atmosphere on Synthesis of Nanostructure TiAl (γ) Alloy by Mechanical Alloying Process
چکیده انگلیسی مقاله In this research, the high-energy planetary mill was employed to produce nanocrystalline Ti-50Al(γ)(at%) powders. Initial powders were mechanically alloyed in 99.9999% and 90% purities of Argon and also Air atmosphere with alloying times up to 50h. The effect of impurity of Argon atmosphere on the microstructure and the rate of phase transformation of Ti-50Al were investigated during mechanical alloying and after annealing at 1000°c. The results showed that the formation of nanostructure TiAl(γ) phase had directly related to the impurities of atmosphere in vials. The impurity of the atmosphere could delay the rate of amoprphization during mechanical alloying and decrease the rate of mechanical alloying process beside some unwanted phases which were produced in powder mixture. The powder particles produced in the high purity Argon atmosphere seemed to be finer than those in the atmosphere. The X-ray patterns, SEM analysis, changes in grain size and DTA test were studied during mechanical alloying and after annealing.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله f عباسی نرگسی | abbasi nargesi
matrials engineering faculty, sahand university of technology, tabriz, i. r. iran
سازمان اصلی تایید شده: دانشگاه صنعتی سهند (Sahand university of technology)

r آذری خسروشاهی آذری خسروشاهی | r azari khosroshahi azari khosroshahi
matrials engineering faculty, sahand university of technology, tabriz, i. r. iran
سازمان اصلی تایید شده: دانشگاه صنعتی سهند (Sahand university of technology)

n پروینی احمدی | parvini ahmadi
matrials engineering faculty, sahand university of technology, tabriz, i. r. iran
سازمان اصلی تایید شده: دانشگاه صنعتی سهند (Sahand university of technology)

نشانی اینترنتی http://www.ijnnonline.net/article_3906_c30d85ce3d48cf189abeb037338e2d94.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات