عنوان انگلیسی Solubility Study in Ag-Cu Binary System Prepared By Ball Milling Process
چکیده انگلیسی مقاله Solid solutions of Ag-Cu were prepared via ball milling process, for about 5-30 h. The Cu-20at%Ag and Cu-3.64at%Ag composition were investigated by X-ray diffraction technique. It was realized that the solid solubility level could be increased by increasing the initial solute content in the mixture. In addition, shifts in peak positions of silver and copper were observed with milling time. The dissolution volume was estimated by thermodynamic relations and was compared with the measured values using X-ray diffraction technique and it was observed that the measured and calculated volumes agreed well. The final dissolution volume of 39.155 litters was calculated by thermodynamic relationship.
کلیدواژه‌های انگلیسی مقاله Copper,Silver,Solid Solution,Mechanical alloying
نویسندگان مقاله سید محمد مهدی شفیعی | s m m
materials and energy research center merc

e صلاحی |
materials and energy research center merc

سید علی طیبی فرد | s a tayebi fard
materials and energy research center merc

نشانی اینترنتی http://www.ijnnonline.net/article_3915_b19709e74907538e9dd66bbf846d9632.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات