International Journal of Nanoscience and Nanotechnology (IJNN)، جلد ۷، شماره ۴، صفحات ۱۹۷-۲۰۰
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Magnetic iron oxide nanoparticles, Polyethylene glycol, Surfactant, Superparamagnetic, Chemical co-precipitation
چکیده انگلیسی مقاله In this study, magnetic iron oxide nanoparticles (Fe3O4) with the size range of 20-30 nm were prepared by the modified controlled chemical co-precipitation method from the solution of ferrous/ferric mixed salt-solution in alkaline medium. In this process polyethylene glycol was used as a surfactant to prevent the solution from agglomeration. The prepared magnetic nanoparticles were characterized by X-ray diffraction (XRD) analysis, scanning electron microscopy (SEM) and vibrating-sample magnetometer (VSM). XRD image indicates the sole existence of inverse cubic spinel phase of magnetic iron oxide nanoparticles (Fe3O4). SEM image show that the dimension of magnetic iron oxide nanoparticles (Fe3O4) is about 24 nm. VSM patterns demonstrate superparamagnetic properties of magnetic nanoparticles.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله z خیاط سرکار | khayat sarkar
kimiya pajooh afagh-e- kavir research amp;amp; technology company, yazd, i. r. iran

f خیاط سرکار | khayat sarkar
kimiya pajooh afagh-e- kavir research amp;amp; technology company, yazd, i. r. iran

نشانی اینترنتی http://www.ijnnonline.net/article_3932_5f9270c032e602afd9e98e3be1e79188.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات