عنوان انگلیسی Preparation and Characterization of Aligned and Random Nanofibrous Nanocomposite Scaffolds of Poly (Vinyl Alcohol), Poly (e-Caprolactone) and Nanohydroxyapatite
چکیده انگلیسی مقاله Nanofibrous scaffolds produced by electrospinning have attracted much attention, recently. Aligned and random nanofibrous scaffolds of poly (vinyl alcohol) (PVA), poly (ε-caprolactone) (PCL) and nanohydroxyapatite (nHA) were fabricated by electrospinning method in this study. The composite nanofibrous scaffolds were subjected to detailed analysis. Morphological investigations revealed that the prepared nanofibers have uniform morphology and the average fiber diameters of aligned and random scaffolds were 135.5 and 290 nm, respectively. The obtained scaffolds have a porous structure with porosity of 88 and 76 % for random and aligned nanofibers, respectively. Furthermore, FTIR analysis demonstrated that there were strong intramolecular interactions between the molecules of PVA/PCL/nHA. On the other hand, mechanical characterizations show that aligning the nanofibers, could significantly improve the rigidity of the resultant biocomposite nanofibrous scaffolds. The results indicate that aligned scaffolds are suitable for tissue engineering applications.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله a doustgani |
biotechnology group, chemical engineering department, tarbiat modares university, tehran, i. r. iran
سازمان اصلی تایید شده: دانشگاه تربیت مدرس (Tarbiat modares university)

e واشقانی فراهانی | vasheghani farahani
biotechnology group, chemical engineering department, tarbiat modares university, tehran, i. r. iran
سازمان اصلی تایید شده: دانشگاه تربیت مدرس (Tarbiat modares university)

m سلیمانی |
department of hematology, faculty of medicine, tarbiat modares university, tehran, i. r. iran
سازمان اصلی تایید شده: دانشگاه تربیت مدرس (Tarbiat modares university)

s هاشمی نجف آبادی | hashemi najafabadi
biotechnology group, chemical engineering department, tarbiat modares university, tehran, i. r. iran
سازمان اصلی تایید شده: دانشگاه تربیت مدرس (Tarbiat modares university)

نشانی اینترنتی http://www.ijnnonline.net/article_3936_a8878ff5982c9f66b5d8cf52694a46af.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات