عنوان انگلیسی A Parametric Study of the Synthesis of Silica Nanoparticles via Sol-Gel Precipitation Method
چکیده انگلیسی مقاله In this study, SiO2 nanoparticles were successfully synthesized via sol-gel precipitation method and the effects of different parameters such as temperature, ethanol, ammonia and tetraethylorthosilicate (TEOS) contents based on water were investigated in a systematic way applying Taguchi experimental design method. It was found that, among all the investigated parameters, ethanol as a co-solvent, had the greatest significant effect on the size of the synthesized silica nanoparticles, so that increasing the amount of ethanol led to initially bigger and then smaller particle size. Temperature had an inverse effect on the particle size, i.e. particle size decreased by increasing the temperature. In addition, the remaining variables, TEOS and ammonia, showed similar trends to that of ethanol in two opposing ways. This novel exploration of size distribution (SD) indicated that particle size was proportional to the SD, so that the narrowest SD was attained at the lowest particle size and vice versa.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله محمدعلی دباغیان | m a
nanostructured materials research center nmrc , sahand university of technology sut , tabriz, i. r. iran
سازمان اصلی تایید شده: دانشگاه صنعتی سهند (Sahand university of technology)

علی اکبر بابالو | a a
nanostructured materials research center nmrc , sahand university of technology sut , tabriz, i. r. iran institute of polymeric materials, sahand university of technology sut , tabriz, i. r. iran
سازمان اصلی تایید شده: دانشگاه صنعتی سهند (Sahand university of technology)

p هادی |
nanostructured materials research center nmrc , sahand university of technology sut , tabriz, i. r. iran institute of polymeric materials, sahand university of technology sut , tabriz, i. r. iran
سازمان اصلی تایید شده: دانشگاه صنعتی سهند (Sahand university of technology)

e جنت دوست |
nanostructured materials research center nmrc , sahand university of technology sut , tabriz, i. r. iran institute of polymeric materials, sahand university of technology sut , tabriz, i. r. iran
سازمان اصلی تایید شده: دانشگاه صنعتی سهند (Sahand university of technology)

نشانی اینترنتی http://www.ijnnonline.net/article_3974_21838560336c4e57c98b791061288453.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات