عنوان انگلیسی Effects of MWCNTs Dispersion on the Microstructure of Sol-Gel Derived Hydroxyapatite
چکیده انگلیسی مقاله Stable homogeneous dispersions of carbon nanotubes (CNTs) were prepared using ethanol as dispersing agent. Then, using sol-gel method, dispersion in the hydroxyapatite matrix and its effects on the microstructure were investigated. The phase composition, chemical structure and morphological and size analyses were performed using XRD, FT-IR, SEM, TEM/SAED/EDX and Raman spectroscopy. The influences of different dispersing agents (sodium dodecyl sulfate (SDS) as a benchmark for future dispersion experiments) and excitation wavelength are discussed and the results are compared with the commonly used UV-Visible spectroscopic analysis. The results indicated that the synthesis of hydroxyapatite particles in the presence of carbon nanotubes had the best effect on the homogenization of carbon nanotube dispersion. The average crystallite size of heat-treated (at 600°C) samples, estimated by Scherrer,s equation, was found to be ~50-60 nm that was confirmed by TEM.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله j jaafaripour میبدی | jaafaripour maybody
department of materials engineering, islamic azad university, tehran, i. r. iran
سازمان اصلی تایید شده: دانشگاه آزاد اسلامی علوم و تحقیقات (Islamic azad university science and research branch)

a نعمتی |
department of materials science and engineering, sharif university of technology, tehran, i. r. iran
سازمان اصلی تایید شده: دانشگاه صنعتی شریف (Sharif university of technology)

e صلاحی |
materials and energy research center, tehran, i. r. iran

محمدحسین امین | m h
materials and energy research center, tehran, i. r. iran

نشانی اینترنتی http://www.ijnnonline.net/article_3984_bba5c06c7d8fd0a4c85df45858a14f92.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات