عنوان انگلیسی Preparation of Flame Retardant Polystyrene via In-Situ Bulk Polymerization Method and Evaluation of its Flammability Properties
چکیده انگلیسی مقاله In this study, in-situ bulk polymerization was investigated for obtaining flame retardant polystyrene (PS). The halogenated and phosphoric compounds were used as flame retardant additives and Perkadox 30 was used as a synergist. The flammability of the PS was evaluated by thermogravimetric analyzer (TGA), limiting oxygen index (LOI) and UL-94 tests. The results show that polymerization process for production of flame retardant polystyrene needs lower amount of flame retardant additives compare with the process for production of flame retardant composites. Furthermore, using Perkadox 30 as a synergist lowers the loading of flame retardant additives. LOI tests show that flame retardant polystyrene synthesized by adding at least 0.35 % (w/w) hexabromocyclododecane (HBCD) during polymerization. TGA analysis confirms that with addition of HBCD the degradation temperature decreases and weight loss occurs quickly. The degradation tempresure of the sample consist of 0.8 % (w/w) HBCD was lower than the sample consist of 0.35 % (w/w) HBCD and 0.45 % (w/w) triphenylphosphate (TPP). The pure polystyrene didn’t pass the UL-94 test because of inflammability and greater dripping. For samples with HBCD, shorter time needed to quench the flame and these samples passed the UL-94 test. On the other hand, greater dripping of polymer melt led to transmission of UL-94 rate from V0 to V2. It is also observed that flaming rate for samples with TPP was very low and dripping didn’t occur.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله سید جمال الدین پیغمبردوست | seyed jamaleddin
faculty of chemical and petroleum engineering, university of tabriz
سازمان اصلی تایید شده: دانشگاه تبریز (Tabriz university)

رامین فریدوند |
faculty of chemical and petroleum engineering, university of tabriz
سازمان اصلی تایید شده: دانشگاه تبریز (Tabriz university)

ابوالفضل شناور |
r amp;amp;d centre of tabriz petrochemical complex tpc

نشانی اینترنتی http://www.ijche.com/article_38869_514b12121881105bb741268fdd38cac5.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات