عنوان انگلیسی Production of Nanosized Synthetic Rutile from Ilmenite Concentrate by Sonochemical HCl and H2SO4 Leaching
چکیده انگلیسی مقاله Titanium dioxide is widely used in the manufacturing of paints, varnishes, lacquer, paper, paperboard, printing inks, rubber, floor covering, and ceramics and so on. White titanium dioxide pigment has been produced by two main processes. The sulfate and the chloride processes. Each of these two routes requires different feedstocks. However, economic and environmental pressures are shifting the world balance of titanium dioxide production away from sulphate based manufacture towards the more cost effective and cleaner chloride route. According to usage of titanium dioxide, the nano sized TiO2 was produced by the sulfuric acid and hydrocholoric acid leaching by using Sonochemical technique during the leaching process. No adding extra materials and no milling after precipitate, no vaporization during the leaching are advantages of this work which reduced the processes of leaching. All of determination techniques of particle size (Zeta Sizer, XRD, SEM, and TEM) prove this matter. The particles sizes of nano TiO2which was leached by HCl and H2SO4 are 83 and 85 nm respectively.
کلیدواژه‌های انگلیسی مقاله Sonochemical,Acid leaching,Nanosize,TiO2,ilmenite
نویسندگان مقاله راضیه رضوی |
department of chemistry, shahid bahonar university of kerman, kerman, i.r. iran
سازمان اصلی تایید شده: دانشگاه شهید باهنر (Shahid bahonar university)

سید محمد علی حسینی | sayed mohammad ali
department of chemistry, faculty of science, jiroft university, jiroft, i.r. iran
سازمان اصلی تایید شده: دانشگاه جیرفت (Jiroft university)

محمد رنجبر |
department of mining engineering, shahid bahonar university of kerman, kerman, i.r. iran
سازمان اصلی تایید شده: دانشگاه شهید باهنر (Shahid bahonar university)

نشانی اینترنتی http://www.ijcce.ac.ir/article_10749_9fba9c2b014c0f0b251430f66ca7e4c9.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات