Iranian Journal of Chemistry and Chemical Engineering، جلد ۲۹، شماره ۴، صفحات ۵۷-۶۵
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Synthesis and Thermal Properties of Novel Biodegradable ABCBA Pentablock Copolymers from Poly (Ethylene glycol), L-Lactide and p-Dioxanone
چکیده انگلیسی مقاله In this work, new biodegradable ABCBA type pentablock copolymers with different mole ratio of L-lactide and PPDO-b-PEG-b-PPDO triblock copolymer were synthesized and characterized. In the first step, PPDO-b-PEG-b-PPDO triblock copolymer was synthesized via a ring-opening polymerization of P-DiOxanone (PDO) monomer with Poly (Ethylene Glycol) (PEG) using stannous octoate (Sn(Oct)2) as the catalyst. In the second step, L-lactide monomers (60 or 80 mole ratio) as the end blocks were added to the resulting prepolymer in presence of stannous octoate (Sn(Oct)2) catalyst. In the first step, Poly (Ethylene Glycol) (PEG) and, in the second step, triblock copolymer acts as the macro-initiator. The obtained pentablock copolymers were identified by 1H and 13CNMR spectroscopy. Intrinsic viscosity of the resulting copolymers was measured via dilute solution viscometry in chloroform as the solvent. The thermal properties (such as melting points, melting enthalpy and crystallinity) and thermal degradation behavior were studied by Differential Scanning Calorimetry (DSC) and Thermal Gravimetric Analysis (TGA). From the obtained results, it was seen that the poly (L-lactide) end blocks show similar crystallization behavior like poly (L-lactide) homopolymer and also melting temperature of pentablock copolymers rise with an increase in L-lactide content.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله جمشید محمدی rovshandeh | mohammadi rovshandeh
caspian faculty of engineering, university of tehran, p.o. box 43841-119 rezvanshahr, i.r. iran
سازمان اصلی تایید شده: دانشگاه تهران (Tehran university)

مجید عبدوس |
department of chemistry, amirkabir university of technology, tehran, i.r. iran
سازمان اصلی تایید شده: دانشگاه صنعتی امیرکبیر (Amirkabir university of technology)

سید مهدی حسینی | sayed mehdi
department of chemistry, amirkabir university of technology, tehran, i.r. iran
سازمان اصلی تایید شده: دانشگاه صنعتی امیرکبیر (Amirkabir university of technology)

محمد ایمانی |
iran polymer and petrochemical institute, tehran, i.r. iran

کامل اخلاصی کزج | ekhlasi kazaj
department of chemistry, faculty of science, guilan universiry, rasht, i.r. iran

نشانی اینترنتی http://www.ijcce.ac.ir/article_6405_0c0964749e0363d7a970ebaf9d9cb6ce.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات