عنوان انگلیسی Preparation and Properties of Polycaprolactone/Poly (Butylene Terephthalate) Blend
چکیده انگلیسی مقاله Polycaprolactone (PCL) and poly(butylene terephthalate) (PBT) blend was prepared by melt processing. The PCL/PBT blend showed similar morphology with that of pure PCL.The crystallization temperature of PCL was increased by the incorporation of PBT. It was also observed that the peak height in the DSC thermograms decreased and then disappeared by adding 40 % or more PBT which might be due to the transestrification between –OH end groups of PCL and ester groups of PBT. The size of PCL spherulites was about 13 µm which decreased highly in the case of blends due to the nucleation effect. The thermal stability of the PCL/PBT blend was higher than pure PCL.
کلیدواژه‌های انگلیسی مقاله Polycaprolactone,Blend,morphology,Thermal properties
نویسندگان مقاله khalid saeed |
department of chemistry, university of malakand, chakdara dir l , khyber pukhtoonkhwa, pakistan

soo یانگ سونگ گو | soo young
department of polymer science, kyungpook national university, 1370 sankyuk-dong, buk-gu, daegu 702-701, south korea

نشانی اینترنتی http://www.ijcce.ac.ir/article_6639_a86491fe3fd4c8efee4e7f7438fb064a.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات