عنوان انگلیسی Effect of Fiber Surface Treatment on Wear Characteristics of Carbon Fiber Reinforced Polyamide 6 Composites
چکیده انگلیسی مقاله Ozone modification method and air-oxidation were used for the surface treatment of polyacrylonitrile(PAN)-based carbon fiber. The surface characteristics of carbon fibers were characterized by X-ray photoelectron spectroscopy (XPS). The interfacial properties of carbon fiber reinforced polyamide 6 (CF/PA6) composites were investigated by means of the single fiber pull-out tests. As a result, it was found that IFSS values of the composites with ozone treated carbon fiber are increased by 60% compared to that without treatment. XPS results show that ozone treatment increases the amount of carboxyl groups on carbon fiber surface, thus the interfacial adhesion between carbon fiber and PA6 matrix is effectively promoted. The effect of surface treatment of carbon fibers on the tribological properties of CF/PA6 composites was comparatively investigated. Experimental results revealed that surface treatment can effectively improve the wear resistance of CF/PA6.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله behroz bayati |
nanostructure materials research center nmrc , sahand university of technology, p.o. box 51335-1996 tabriz, i.r. iran
سازمان اصلی تایید شده: دانشگاه صنعتی سهند (Sahand university of technology)

نشانی اینترنتی http://www.ijcce.ac.ir/article_9911_d4b2749d1db72373c6c950cbb8b63805.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات