عنوان انگلیسی Synthesis and Seeding Time Effect on the Inter-Crystalline Structure of Hydroxy-Sodalite Zeolite Membranes by Single Gas (H2 and N2) Permeation
چکیده انگلیسی مقاله Microporous hydroxy-sodalite zeolite membranes with different morphologies were synthesized via secondary growth technique with vacuum seeding on tubular α-Al2O3 supports at two different synthesis conditions (i.e. two different routes). Microstructures of the synthesized membranes were characterized by X-ray diffraction (XRD), Scanning electron microscope (SEM) and single gas permeation using H2 and N2. Also, the effect of seeding time on microstructure and performance of the synthesized hydroxy-sodalite top-layers was investigated at four different levels (60, 120, 180 and 240 s). Permeation test was carried out in order to attain a more exact comparison of both applied routes and seeding times. Microstructure of the synthesized hydroxy-sodalite zeolite membrane layers and the effects of the investigated factors on the elimination of inter-crystalline pores were evaluated by the permeation of single gases (H2 and N2) under different pressure differences at ambient temperature. The permeation results confirmed the high quality of the hydroxy-sodalite zeolite membranes manufactured via the first route at seeding time of 60s for the hydrogen purification under extremely low temperatures (< 200 K) and/or extremely high pressures (> 100 bars).
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله behroz bayati |
nanostructure materials research center nmrc , sahand university of technology, p.o. box 51335-1996 tabriz, i.r. iran
سازمان اصلی تایید شده: دانشگاه صنعتی سهند (Sahand university of technology)

علی اکبر بابالو | ali akbar
nanostructure materials research center nmrc , sahand university of technology, p.o. box 51335-1996 tabriz, i.r. iran
سازمان اصلی تایید شده: دانشگاه صنعتی سهند (Sahand university of technology)

پژمان احمدیان نمینی | pejman ahmadian
nanostructure materials research center nmrc , sahand university of technology, p.o. box 51335-1996 tabriz, i.r. iran
سازمان اصلی تایید شده: دانشگاه صنعتی سهند (Sahand university of technology)

نشانی اینترنتی http://www.ijcce.ac.ir/article_6734_ed398dd610b8fcbd9052def50aeda26a.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات