عنوان انگلیسی Preparation and Characterization of WO3 Electrochromic Films Obtained by the Sol-Gel Process
چکیده انگلیسی مقاله Tungsten trioxide (WO3) films have been coated on indium thin oxide (ITO) conductive glass substrate, using aqueous solution of peroxotungstic acid (PTA) by the sol-gel dip coating method. X-ray diffractometery (XRD) analysis confirmed monoclinic and triclinic structure for the film and powdered WO3 respectively. Fourier transforms infrared spectroscopy (FT-IR) exhibited the structure of peroxotungstic acid. The SEM micrograph of annealed species revealed micro cracks due to decrease of density and contraction of layers. Energy- dispersive X-ray (EDX) study determined 1:3 ratios of oxygen and tungsten atoms in the prepared films at heat treatment temperature higher than 200ºC. The electrochromical behavior was investigated in 1M HCL solution employing cyclic voltammetry. It was found that WO3 films demonstrated good reversibility at 200 ºC.
کلیدواژه‌های انگلیسی مقاله Sol-gel,Tungsten oxide,Thin film,Electrochromic,coating
نویسندگان مقاله معصومه شربتداران |
material and ion beam application division, nuclear research center, p. o. box 31485-498, karaj, i.r. iran

عبدالجواد نوین روز |
material and ion beam application division, nuclear research center, p. o. box 31485-498, karaj, i.r. iran

حسن noorkojouri |
material and ion beam application division, nuclear research center, p. o. box 31485-498, karaj, i.r. iran

نشانی اینترنتی http://www.ijcce.ac.ir/article_8076_50053b700efc92b4a0f853c38e12b0d5.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات