Iranian Journal of Materials Forming، جلد ۳، شماره ۱، صفحات ۱-۱۱
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Finite element analysis of elastic-plastic solids under Vickers indentation: surface deformation
چکیده انگلیسی مقاله Finite element modeling has been used to study the development of surface deformation during indentation with a Vickers indenter. A wide range of materials with different elastic modulus and yield stresses are examined. Results show that in a pyramidal indentation process, for a perfectly plastic material, sinking-in during loading can change to pile-up in unloading. This phenomenon depends on the elastic modulus to yield stress ratio. Results also show that the amount of pile-up cannot be related solely to the strain-hardening exponent, as often assumed. Rather, after initially sinking-in at small depths of penetration, the pile-up for many materials evolves and increases gradually as the indenter is driven into the material. It is shown that the ratio of the plastic volume radius to the indentation depth is nearly constant during loading and it is a function of the yield stress and the Young modulus. Experimental verification in loading and unloading is carried out with the results of Alcala et al. (Acta Materialia, 2000, pp. 3451).
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله علی نایبی |
shiraz university
سازمان اصلی تایید شده: دانشگاه شیراز (Shiraz university)

نشانی اینترنتی http://ijmf.shirazu.ac.ir/article_3678_116f1252d70896e5b27396cdf72a8afc.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات