Iranian Journal of Materials Forming، جلد ۳، شماره ۱، صفحات ۶۵-۷۴
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Superplasticity of a fine-grained Mg–1.5 wt% Gd alloy after severe plastic deformation
چکیده انگلیسی مقاله The strain rate sensitivity (SRS) of Mg–1.5 wt% Gd processed by conventional extrusion and 2 passes of simple shear extrusion (SSE) was investigated by shear punch testing. Shear punch tests were conducted at initial shear strain rates in the range of 0.003–0.3 s-1 and at temperatures in the range of 573–773 K. A fine-grained microstructure with an average grain size of about 2.5 µm, obtained after 2 passes of SSE, resulted in high SRS index (m-value) of 0.4 at 723 K. The calculated activation energy for 2 passes deformed alloy is 116 kJ/mol which is higher than the activation energy of grain boundary diffusion in magnesium (75 kJ/mol). This higher amount of activation energy can be attributed to the presence of gadolinium in this alloy. This SRS index together with an activation energy of 116 kJ/mol are indicative of a superplastic deformation behavior dominated by grain boundary sliding accommodated by grain boundary diffusion at 723 K.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله نازنین بیات ترک | bayat tork
school of metallurgy and materials engineering, iran university of science and technology
سازمان اصلی تایید شده: دانشگاه علم و صنعت ایران (Iran university of science and technology)

سید حسین رضوی | seyed hossein
school of metallurgy and materials engineering iran university of science amp;amp;amp; technology

حسن ثقفیان |
school of metallurgy and materials engineering, iran university of science and technology
سازمان اصلی تایید شده: دانشگاه علم و صنعت ایران (Iran university of science and technology)

رضا محمودی |
school of metallurgical and materials engineering, college of engineering, university of tehran, tehran, iran
سازمان اصلی تایید شده: دانشگاه تهران (Tehran university)

نشانی اینترنتی http://ijmf.shirazu.ac.ir/article_3711_96eeccc261b702222eaef85e5380d8e2.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات