Iranian Journal of Materials Forming، جلد ۲، شماره ۱، صفحات ۳۰-۴۲
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Hot and Cold Tensile Behavior of Al 6061 Produced by Equal Channel Angular Pressing and Subsequent Cold Rolling
چکیده انگلیسی مقاله The full annealing AA6061 aluminum alloy was subjected to severe plastic deformationvia the combination of equal channel angular pressing (ECAP) and cold rolling (CR) in order torefine its microstructure and to improve its mechanical properties. According to the results of hotand cold tensile tests, the combination of ECAP and CR significantly affected the final strengthand ductility of studied AA6061. Four passes of ECAP followed by 90% reduction in rolling led toabout 5.4 and 3.15 times increase in the yield and ultimate tensile strengths, respectively. Inaddition, the hot ductility and strain rate sensitivity were increased by applying ECAP plus CR.The changes in mechanical properties were attributed to the enhanced dislocation density and tothe reduced grain size. The results show that a decrease in grains/subgrains size (0.37 μm) and anincrease in the fraction of high angle grain boundaries, exhibited significant effect on the hotductility of higher severe plastic deformed sample.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله علی اکبر khamei | a a
department of mining and metallurgical engineering, amirkabir university of technology, tehran, iran
سازمان اصلی تایید شده: دانشگاه صنعتی امیرکبیر (Amirkabir university of technology)

k دهقانی |
department of mining and metallurgical engineering, amirkabir university of technology, tehran, iran
سازمان اصلی تایید شده: دانشگاه صنعتی امیرکبیر (Amirkabir university of technology)

s بخشی |
metallic materials research center mmrc-ma , malkashtar university, tehran, iran

k کلایه |
department of mechanical engineering, university of maryland, baltimore county, usa

نشانی اینترنتی http://ijmf.shirazu.ac.ir/article_2913_beec88126108ad78d4953398d9866bb8.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات