عنوان انگلیسی Static Strain Aging Behavior of Low Carbon Steel Drawn Wire
چکیده انگلیسی مقاله The static strain aging is a phenomenon that can change the mechanical properties of low carbon steels. Thus, the static strain aging behavior of low carbon steel wires after drawing process is studied. To do so, the wires are austenitized at different temperatures and cooled in different rates. Then the wires are drawn and aged at a specific temperature and time. Before and after aging of each drawn wire, the hardness distribution at its cross section is measured. The increase in hardness due to aging is called aging index. The results show that the hardness of drawn wire is increased from center to surface of its cross section. However, after aging the hardness is decreased from center to surface. In addition, with increasing the austenitizing temperature, the index is increased. Also, with increasing the cooling rate, the index is decreased. Moreover, the aging index is decreased from center to surface.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله m کاظمی نژاد |
sharif university of technology
سازمان اصلی تایید شده: دانشگاه صنعتی شریف (Sharif university of technology)

y khaledzadeh |
sharif university of technology
سازمان اصلی تایید شده: دانشگاه صنعتی شریف (Sharif university of technology)

a کریمی طاهری | karimi taheri
sharif university of technology
سازمان اصلی تایید شده: دانشگاه صنعتی شریف (Sharif university of technology)

نشانی اینترنتی http://ijmf.shirazu.ac.ir/article_2491_9180fa1cb15091df19acce20d9c51380.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات