عنوان انگلیسی Formation of a solid solution through accumulative roll bonding (ARB) and post-heat treatment of multilayered Cu/Zn/Al
چکیده انگلیسی مقاله In the present study, the capability of accumulative roll bonding (ARB) and subsequent heat-treatment to fabricate solid solution from a multilayered Cu/Zn/Al was investigated. Two post-heat treatment (one-step and two-step) routes were proposed. In the first, the ARB processed material was heated to 800 C for 5:30 hours and allowed to cool slowly in a furnace (one-step route). In the second (two-step route), the composite was heated to 800 C for 3 hours and quenched in the cold water (0 ºC). The microstructures were characterized using a field emission scanning electron microscope (SEM) equipped with energy dispersive x-ray detector (EDX). The x-ray diffraction (XRD) pattern was used to identify the phases. Results showed that even after imposing high ARB cycles (up to 14 cycles), the solid solution could not be formed so far. However, after the subsequent heat-treatment, Cu, Zn and Al distributed uniformly in the microstructure and a copper-based solid solution was formed.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله m ریحانیان |
department of materials science and engineering, faculty of engineering, shahid chamran university, ahvaz, iran
سازمان اصلی تایید شده: دانشگاه شهید چمران (Shahid chamran university)

محمد مهدی مهدویان | m m
islamic azad university, ahvaz, iran
سازمان اصلی تایید شده: دانشگاه آزاد اسلامی علوم و تحقیقات (Islamic azad university science and research branch)

l قلندری |
islamic azad university, shiraz, iran
سازمان اصلی تایید شده: دانشگاه آزاد اسلامی علوم و تحقیقات (Islamic azad university science and research branch)

a عبیداوی |
islamic azad university, ahvaz, iran
سازمان اصلی تایید شده: دانشگاه آزاد اسلامی علوم و تحقیقات (Islamic azad university science and research branch)

نشانی اینترنتی http://ijmf.shirazu.ac.ir/article_2277_c811ae8fc84b7be0ed5e62c4fa8384ea.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات