عنوان انگلیسی EFFECT OF NICKEL AND COBALT ADDITIONS ON INFILTRATION BEHAVIOR, MICROSTRUCTURE AND HARDNESS OF W-AG COMPOSITES
چکیده انگلیسی مقاله In this research, infiltration behavior of W-Ag composite compacts with Nickel and Cobalt as additives has been investigated. Nickel and Cobalt were added to Tungsten powder by two distinct methods: mixing elementally and reduction of salt solution. The coated Tungsten powders were compacted under controlled pressures to make porous skeleton with 32-37 vol. % porosity. Infiltration process was carried out at 1100 ̊C under a reducing atmosphere for 1h. The effect of additives on infiltration of Ag and density were evaluated by SEM and Archimedes methods. Properties of the specimens were compared following two distinct processes namely: I) sintering simultaneously with infiltration process and II) sintering prior to infiltration (pre-sintering process). It was found that specimens which were pre-sintered and then infiltrated with molten silver represent higher hardness and finer microstructure than the specimens infiltrated simultaneously with sintering.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله n پروین | n parvin
department of mining and metallurgical engineering, amirkabir university of technology, tehran, iran.

سازمان اصلی تایید شده: دانشگاه صنعتی امیرکبیر (Amirkabir university of technology)

r درخشنده حقیقی | r derakhshandeh haghighi
department of mining and metallurgical engineering, amirkabir university of technology, tehran, iran.

سازمان اصلی تایید شده: دانشگاه صنعتی امیرکبیر (Amirkabir university of technology)

m نعیمی | m naeimi
department of mining and metallurgical engineering, amirkabir university of technology, tehran, iran.

سازمان اصلی تایید شده: دانشگاه صنعتی امیرکبیر (Amirkabir university of technology)

r پرستار نمین | r parastar namin
department of mining and metallurgical engineering, amirkabir university of technology, tehran, iran.

سازمان اصلی تایید شده: دانشگاه صنعتی امیرکبیر (Amirkabir university of technology)

محمد مهدی هادوی | m m hadavi
department of mining and metallurgical engineering, amirkabir university of technology, tehran, iran.

سازمان اصلی تایید شده: دانشگاه صنعتی امیرکبیر (Amirkabir university of technology)

نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-127-57&slc_lang=en&sid=en
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده گروه مهندسی مواد . مباحث ویژه
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات