عنوان انگلیسی INVESTIGATING THE CORROSION BEHAVIOR OF NANO STRUCTURED COPPER STRIP PRODUCED BY ACCUMULATIVE ROLL BONDING (ARB) PROCESS IN ACIDIC CHLORIDE ENVIRONMENT
چکیده انگلیسی مقاله In this research accumulative roll bonding process as sever plastic deformation process was applied up to 8 cycles to produce the ultrafine grain copper. Microstructure of cycle 1, cycle 4 and cycle 8 investigated by TEM images. By analyzing TEM images the grain size measured below 100 nm in cycle 8 and it was with an average grain size of 200 nm. Corrosion resistance of rolled copper strips in comparing with unrolled copper strip was investigated in acidic (pH=2) 3.5 wt. % NaCl solution. Potentiodynamic polarization and EIS tests used for corrosion resistance investigations. The corrosion morphologies analyzed by FE-SEM microscopy after polarization test and immersion for 40 hours. Results show that the corrosion resistance decreased up to cycle 2 and increased after rolled for forth time. The corrosion degradation was more intergranular in cycle 2 and unrolled counterpart. It was more uniform rather than intergranular type in cycle 8. Corrosion current density in unrolled sample (2.55 µAcm -2 ) was about two times of that in cycle 8 (1.45 µAcm -2 ). The higher corrosion rate in cycle 2 in comparison with others was attributed to unstable microstructure and increase in dislocation density whereas the uniform corrosion in cycle 8 was due to stable UFG formation
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله a nikfahm | a nikfahm
department of technical inspection engineering, abadan faculty of petroleum engineering, petroleum university of technology, abadan, iran.


i دانایی | i danaee
department of technical inspection engineering, abadan faculty of petroleum engineering, petroleum university of technology, abadan, iran.


a اشرفی | a ashrafi
department of materials engineering, faculty of engineering, shahid chamran university, ahvaz, iran.

سازمان اصلی تایید شده: دانشگاه شهید چمران (Shahid chamran university)

محمد رضا طرقی نژاد | m r toroghinejad
department of materials engineering, isfahan university of technology, isfahan, iran.

سازمان اصلی تایید شده: دانشگاه صنعتی اصفهان (Isfahan university of technology)

نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-127-49&slc_lang=en&sid=en
فایل مقاله دریافت فایل مقاله
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده گروه مهندسی مواد . مباحث ویژه
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات