Iranian Journal of Materials Science and Engineering، جلد ۹، شماره ۳، صفحات ۳۳-۳۹
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Heat Treatment Of Cobalt-Base Alloy Surgical Implants With Hydroxyapatite-Bioglass For Surface Bioactivation
چکیده انگلیسی مقاله ASTM F-75 Cobalt-base alloy castings are widely used for manufacturing orthopedic implants. This alloy needs both homogenization and solutionizing heat treatment after casting, as well as bioactivation of the surface to increase the ability of tissue bonding. In this study, ASTM F-75 Cobalt-base substrate was heat treated at 1220°C for 1 hour in contact with Hydroxyapatite-Bioglass powder in order to solutionize and homogenize the microstructure and promote surface bioactivation. For bioactivity evaluation, heat treated specimens were immersed in Simulated Body Fluid (SBF). Surface of specimens before and after the immersion was analyzed by Scanning Electron Microscopy (SEM), Energy Dispersive Spectroscopy (EDX) and X-Ray Diffraction (XRD). Results showed an appropriate microstructure with bioactive layer on the surface of specimens after heat treatment. In vitro result and formation of bone-like apatite layer on specimens indicated that heat treated samples were potentially suitable for bone replacement and tissue regeneration under highly loaded conditions.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله حسین مینویی | hossein minouei
department of materials engineering, isfahan university of technology, isfahan, 8415683111, iran

سازمان اصلی تایید شده: دانشگاه صنعتی اصفهان (Isfahan university of technology)

محمدحسین فتحی | mohammadhossein fathi
department of materials engineering, isfahan university of technology, isfahan, 8415683111, iran

سازمان اصلی تایید شده: دانشگاه صنعتی اصفهان (Isfahan university of technology)

محمود مرآتیان | mahmood meratian
department of materials engineering, isfahan university of technology, isfahan, 8415683111, iran

سازمان اصلی تایید شده: دانشگاه صنعتی اصفهان (Isfahan university of technology)

حسین ghazvinizadeh | hossein ghazvinizadeh
department of materials engineering, isfahan university of technology, isfahan, 8415683111, iran

سازمان اصلی تایید شده: دانشگاه صنعتی اصفهان (Isfahan university of technology)

نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-125-1&slc_lang=en&sid=en
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده گروه سطح پوشش و خوردگی
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات