عنوان انگلیسی LOW TEMPERATURE MOLTEN SALT SYNTHESIS OF NANO CRYSTALLINE MgAl2O4 POWDER
چکیده انگلیسی مقاله Abstract: composition of MgO and nano boehmite. The reactant and potassium chloride, as the reaction media, were fired at800-1000 °C at different dwell times (0.5-5 h) in the ambient atmosphere. After washing and filtration, the spinel nanopowder was characterized by X-ray diffraction (XRD), Scanning electron microscopy (SEM), and Brunauer-Emmett-Teller (BET) techniques. It was demonstrated that the formation temperature decreased to 850 particles revealed an average size of 30 nm with a narrow size distribution. The mechanism of MgAlwas found to be a template type where the morphology and size of product were similar to those of alumina formedfrom boehmite decomposition. Prolonging the reaction time from 0.5 to 3 h, the reaction was further completed andcrystallinity was improved. However, the increase of temperature was more effective in this regard.MgAl2O4 (MA) nano powder was synthesized via molten salt technique, by heating stochiometric°C. The nano spinel2O4 formation
کلیدواژه‌های انگلیسی مقاله Keywords, spinel nano powder, molten salt method, boehmite
نویسندگان مقاله y صفایی نایینی | y safaei naeini
1 school of metallurgy and materials engineering, iran university of science and technology, tehran, iran.

سازمان اصلی تایید شده: دانشگاه علم و صنعت ایران (Iran university of science and technology)

f گلستانی فرد | f golestani fard
center of excellence for advanced materials and processing ceamp , iran university of science and


f خراسانی زاده | f khorasanizadeh


m امین زارع | m aminzare
1 school of metallurgy and materials engineering, iran university of science and technology, tehran, iran.
سازمان اصلی تایید شده: دانشگاه علم و صنعت ایران (Iran university of science and technology)

s زانگ | s zhang
3 department of materials engineering, university of sheffield, sheffield s1 3jd, uk.
نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-3-151&slc_lang=en&sid=en
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده گروه مهندسی مواد . مباحث ویژه
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات