عنوان انگلیسی THERMO-MECHANICAL DESIGN OPTIMIZATION OF CORDIERITE–MULLITE BASED KILN FURNITURE
چکیده انگلیسی مقاله Abstract: Cordierite-Mullite based kiln furnitures are widely used in fast-firing of ceramic products because of their low thermal expansion which confer them a very good ability to thermal shock resistance. Difference in CTE of constituent phase can develop damage during thermal cycling due to internal stresses. Increase in industrial competitiveness leads to the development of new means for extending refractory life and increasing reliability of industrial tools so investigations regarding the structuralmechanical behaviour of refractory systems are becoming essential. In this paper, Thermo-mechanical design of commercial Cordierite-Mullite based kiln furniture was investigated by using finite element method (FEM) and possible solutions for improvement of working life have been considered. The results indicated that the change of the kiln furniture geometry can decrease the maximum thermomechanical stress in study conditions which can prolong the refractory service life. Obtained results indicate the existence of an optimal thickness for the section under maximum thermo-mechanical stress. Increasing filet radius of ring region from 3 to 9 mm decreases thermo-mechanical stress value from 113 to 93 MPa.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله m فرضعلی پور تبریز | m farzalipour tabriz
department of materials engineering, faculty of mechanical engineering, university of tabriz,

سازمان اصلی تایید شده: دانشگاه تبریز (Tabriz university)

m قاسمی کاکرودی | m ghassemi kakroudi
department of materials engineering, faculty of mechanical engineering, university of tabriz,

سازمان اصلی تایید شده: دانشگاه تبریز (Tabriz university)

نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-3-135&slc_lang=en&sid=en
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده technical note
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات