Iranian Journal of Materials Science and Engineering، جلد ۶، شماره ۱، صفحات ۲۶-۳۰
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Mechanochemical synthesis of alumina nanoparticles
چکیده انگلیسی مقاله Abstract: Nano- size alumina particles have been synthesized by mechanical activation of a dry powder mixture of AlCl3 and CaO. Mechanical milling of the above raw materials with the conditions adopted in this study resulted in the formation of a mixture consisting of crystalline CaO and amorphous aluminum chlorides phases. There was no sign of chemical reaction occurring during milling stage as evidenced by x-ray diffraction studies. Subsequent heat treatment of the milled powder at 350ºC resulted in the occurrence of displacement reaction and the formation of Al2O3 particles within a water soluble CaCl2 matrix. The effect of higher temperature calcinations on the phase development in this powder mixture was followed by X-ray diffraction (XRD) analysis and scanning electron microscope ( SEM). Differential thermal analysis (DTA) was used to compare the thermal behavior between the milled and unmilled powders. Perhaps the most important result in this study was the observation of á-Al2O3 phase at a very low temperature of 500ºC.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله m ابراهیمی بسابی | m ebrahimi basabi


j جوادپور | j javadpour
department of metallurgy and materials engineering, iran university of science amp;amp; technology, tehran, iran


حسین رضایی | h rezaie


m گودرزی | m goodarzi


نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-3-47&slc_lang=en&sid=en
فایل مقاله دریافت فایل مقاله
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات