عنوان انگلیسی THERMAL FATIGUE RESISTANCES OF 356 AND 413 CAST Al ALLOYS
چکیده انگلیسی مقاله Abstract: Thermal fatigue is a stochastic process often showing considerable scatter even in controlled environments. Due to complexity of thermal fatigue, there is no a complete analytical solution for predicting the effect of this property on the life of various components, subjected to severe thermal fluctuations. Among these components, one can mention car cylinder, cylinder head and piston which bear damages due to thermal fatigue. All these components are usually produced by casting techniques. In order to comprehend and compare the thermal fatigue resistance of cast Al alloys 356 and 413, this research was designed and performed. For this purpose, several samples in the form of disc were cast from the two alloys in sand mould. The microstructures of the cast samples were studied by light microscopy in order to choose the samples with the least amounts of defects for thermal fatigue tests. The results of thermal fatigue tests showed that the nucleation of microcracks in Al-356 alloy occurred at shorter time relative to those occurred in Al- 413 alloy under the same test conditions. In addition, the density of micro-cracks in Al-356 alloy was more than that of Al-413 alloy. The results of fractography on 356 alloy indicated that the cracks were generally nucleated from inter-dendritic shrinkage porosities and occasionally from the interface of silicon particles with the matrix. The growth of these micro cracks was along the dendrite arms. Fractography of 413 alloy fracture surfaces showed that nucleation of microcracks was often associated with silicon particles.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله مهدی دیواندری | m divandari
department of metallurgy and materials engineering, iran university of science and technology, tehran,iran

سازمان اصلی تایید شده: دانشگاه علم و صنعت ایران (Iran university of science and technology)

h عربی | h arabi


h قاسمی میانایی | h ghasemi mianaei


نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-3-29&slc_lang=en&sid=en
فایل مقاله دریافت فایل مقاله
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات