عنوان انگلیسی EFFECT OF DIFFUSION ANNEALING ON PROPERTIES OF TI/304L STAINLESS STEEL EXPLOSION CLAD
چکیده انگلیسی مقاله In this study, commercially pure titanium/304L stainless steel explosion bonded clads have been annealed under argon atmosphere over the temperature range of 700-900°C for 1h.Microstructure of the clads have been investigated before and after anealing. X-ray diffraction studies revealed that the annealing products in the form of intermetallic phases were gradually formed at the interface of the annealed clads. It was also found that, the bonding zone width increased with temperature according to an Arrhenius type equation. On the base of this equation, the activation energy of bonding zone growth was found equal to about 66.5 kJ/mol. The bond strength of the diffusion annealed clads were evaluated stress relieved. The maximum average tensile strength of ~350MPa was obtained for the as-welded clad. It was found that the bond strength decreased with annealing at 700°C due to an increase in the width of brittle intermetallic layer.
کلیدواژه‌های انگلیسی مقاله ANNEALING, EXPLOSION CLAD, TITANIUM, 304L STAINLESS STEEL
نویسندگان مقاله ابراهیمی a r | ebrahimi a r
department of materials engineering, sahand university of technology, tabriz, iran

سازمان اصلی تایید شده: دانشگاه صنعتی سهند (Sahand university of technology)

یادگاری m | yadegari m


خسروشاهی r a | khosroshahi r a


نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-1-72&slc_lang=fa&sid=en
فایل مقاله دریافت فایل مقاله
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده گروه سرامیک
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات