عنوان انگلیسی Catalytically Graphitized Electrospun Carbon Nanofibers Adorned with Nickel Nanoparticles for Catalysis Applications
چکیده انگلیسی مقاله Catalytically graphitized electrospun carbon nanofibers adorned uniformly with fine nickel nanoparticles were successfully prepared. The procedure was based on the electrospinning technique and the use of nickel precursor to create both graphitized nanofibers and nickel nanoparticles under a relatively low-temperature heat treatment. The X-ray diffraction and Raman results clearly proved catalytic graphitization of polymer-based carbon fibers in the presence of nickel catalyst. Taking the results from scanning and transmission electron microscopies and X-ray diffraction into account, it was inferred that during the heat treatment, nickel atoms have diffused through the nanofibers and formed fine nickel nanoparticles on the surface of graphitized nanofibers to make a well stabilized heterogeneous nanostructure. The results from Brunauer–Emmett–Teller technique also showed a high surface area value of 140.2 m2g-1 for the obtained structure. All these attributes along with the fibrous and porous structure enable the product to serve as a potential candidate in the catalysis applications.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله علی محمد بازرگان | a m
department of polymer engineering and color technology, amirkabir university of technology, 15875-4413 tehran, iran
سازمان اصلی تایید شده: دانشگاه صنعتی امیرکبیر (Amirkabir university of technology)

m اسماعیل پور |
department of materials engineering, isfahan university of technology iut , isfahan, 84156-83111, iran
سازمان اصلی تایید شده: دانشگاه صنعتی اصفهان (Isfahan university of technology)

m کیانپور راد | keyanpour rad
materials and energy research center, p. o. box 14155-4777, tehran, iran

نشانی اینترنتی http://jns.kashanu.ac.ir/article_13642_bb7201fe8a4fea93b5b707b2787a2c91.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات