Journal of Nanostructures، جلد ۵، شماره ۴، صفحات ۴۴۳-۴۵۳
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Fabrication of Novel High Potential Chromium-Doped TiO2 Nanoparticulate Electrode-based Dye-Sensitized Solar Cell (DSSC)
چکیده انگلیسی مقاله In the current study, pure TiO2 and Cr-doped TiO2 (Cr@TiO2) nanoparticles were synthesized via sol-gel method and the resulting materials were applied to prepare the porous TiO2 electrodes for dye-sensitized solar cells (DSSCs). It is hypothesized that the advantages of the doping of the metal ions into TiO2 lattice are the temporary rapping of the photogenerated electron-hole (charge carriers) by the metal dopants and the retarding charge recombination during electron migration from TiO2 to the electrode surface. Spectroscopic and microscopic findings showed that all the prepared samples consist of only anatse phase with average size of 10-15nm. In addition, relative to the bare TiO2, Cr@TiO2 absorption in visible light region was considerably improved due to the surface Plasmon phenomenon. Current-voltage (I-V) curves exhibited that the solar cells made of Cr@TiO2 nanoparticles results in higher photocurrent density than the cells made of bare TiO2. The large improvement of photovoltaic performance of the Cr-doped TiO2 cell stems from negative shift of TiO2 conduction band and retarding charge recombination. Finally, it is concluded that the proposed route in the current study is an effective way to enhance the energy conversion efficiency and overall performance of DSSC.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله a احترام |
department of electrical engineering, kashan branch, islamic azad university, kashan, iran
سازمان اصلی تایید شده: دانشگاه آزاد اسلامی علوم و تحقیقات (Islamic azad university science and research branch)

m همدانیان |
institute of nanosciences and nanotechnology, university of kashan, kashan, iran and department of physical chemistry, faculty of chemistry, university of kashan, kashan, iran
سازمان اصلی تایید شده: دانشگاه کاشان (Kashan university)

v جباری |
institute of nanosciences and nanotechnology, university of kashan, kashan, iran
سازمان اصلی تایید شده: دانشگاه کاشان (Kashan university)

نشانی اینترنتی http://jns.kashanu.ac.ir/article_12579_914d462a80eb657b6099f00aaffb7211.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات