عنوان انگلیسی Fabrication and Electrochemical Behavior of Monoclinic CuO and CuO/Graphite Composite Nanoparticles as Cathode in an Alkaline Zn-CuO Battery
چکیده انگلیسی مقاله Electrochemical properties of various rock-shaped-CuO/graphite (G) composites and monoclinic structure CuO nanoparticles as the cathode versus a zinc plate as the anode in a 4M NaOH electrolyte were elucidated by electrochemical impedance spectroscopy (EIS) and chronopotentiometry (CP) in a two electrode configuration cell. Various values of G 9, 16 and 28 wt% were prepared and studied as cathode materials for an alkaline Zn-CuO Battery. The EIS results demonstrated that increasing the mass ratio of G caused significant decrease in charge transfer resistance (Rct) and capacitive behavior of the electrode. Also, the discharging voltage of the cells was increased due to raising the mass ratio of the graphite. Besides, electrochemical properties of the monoclinic structure CuO nanoparticles as cathode material in the alkaline battery was compared with a rock shaped CuO particles. The results showed that the discharged voltage of monoclinic CuO nanoparticles is less than another rock shaped CuO nanoparticles form.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله y زراعت کیش |
department of chemistry, faculty of science, k.n. toosi university of technology, p.o. box 15875-4416, tehran, iran
سازمان اصلی تایید شده: دانشگاه صنعتی خواجه نصیرالدین طوسی (Khajeh nasir toosi university of technology)

m جعفریان |
department of chemistry, faculty of science, k.n. toosi university of technology, p.o. box 15875-4416, tehran, iran
سازمان اصلی تایید شده: دانشگاه صنعتی خواجه نصیرالدین طوسی (Khajeh nasir toosi university of technology)

مهدی mahjani | m g
department of chemistry, faculty of science, k.n. toosi university of technology, p.o. box 15875-4416, tehran, iran
سازمان اصلی تایید شده: دانشگاه صنعتی خواجه نصیرالدین طوسی (Khajeh nasir toosi university of technology)

نشانی اینترنتی http://jns.kashanu.ac.ir/article_11546_c4f2b11f080534afd6dd187d2180bec2.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات