Journal of Nanostructures، جلد ۳، شماره ۲، صفحات ۱۴۵-۱۵۴
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Synthesis and Characterization of Copper Indium Sulfide Chalcopyrite Structure with Hot Injection Method
چکیده انگلیسی مقاله In this investigation, CuInS2 ternary compound was synthesized by injection of thiourea solution into a hot copper-indium solution. The CuCl, InCl3 along with (SC (NH2)2) were used as a precursor dissolved in high boiling point solvent such as oleylamine (CH(CH2)17NH2) and oleic acid (CH(CH2)16COOH) as a coordination solvent and capping agent, respectively. The size, distribution and shape were optimized by controlling some parameters such as the ratio of solvent to capping agent, anion and cation solution temperature in the instant of injection. The crystal structure, morphology, and optical properties of synthesized nanoparticles were characterized using XRD, TEM, UV-VIS-NIR and PL. The results indicate that the temperature of the solution in the instant of injection has a significant effect on the tuning of the nanocrystals size as well as narrow size distribution.
کلیدواژه‌های انگلیسی مقاله Hot injection,Chalcopyrite,complex,Coordination Solvent
نویسندگان مقاله y وحیدشاد |
school of metallurgy and material engineering, iran university of science and technology, tehran 16844, iran. material research department, engineering research institute, tehran , 16844, iran.
سازمان اصلی تایید شده: دانشگاه علم و صنعت ایران (Iran university of science and technology)

r قاسم زاده |
school of metallurgy and material engineering, iran university of science and technology, tehran 16844, iran.
سازمان اصلی تایید شده: دانشگاه علم و صنعت ایران (Iran university of science and technology)

a ایرجی زاد |
department of physics, sharif university of technology, tehran 11365-9161, iran.
سازمان اصلی تایید شده: دانشگاه صنعتی شریف (Sharif university of technology)

سید محمد میرکاظمی | s m
school of metallurgy and material engineering, iran university of science and technology, tehran 16844, iran.
سازمان اصلی تایید شده: دانشگاه علم و صنعت ایران (Iran university of science and technology)

نشانی اینترنتی http://jns.kashanu.ac.ir/article_5455_6444974acc50c3fa467b9d465ffd976a.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات