عنوان انگلیسی Effect of Calcination Temperature on the Alumina-Zirconia Nanostructures Prepared by Combustion Synthesis
چکیده انگلیسی مقاله In this research, a sol gel autocaombustion route has been proposed to synthesize alumina-zirconia composite powders, using ammonium bicarbonate as a new fuel. Then the effect of calcination temperature on phase transformation and crystallite sizes was investigated. To characterize the products XRD, TEM and BET analyses were used. XRD patterns of as-synthesized powder and calcined powders at 1100 ◦C and 1200 ◦C showed t-ZrO2 phase with small crystallite sizes (sintered at 1300 ◦C and the particle sizes after calcination were 14.90 nm and 50 nm for ZrO2 and Al2O3 phases, respectively as calculated from XRD and the transformation of t-ZrO2 to m-ZrO2 started at 1300 ◦C. TEM micrograph of as-synthesized powder revealed nanosize spherical particles of about 8 nm.
کلیدواژه‌های انگلیسی مقاله Sol-Gel,Autocombustion,Zirconia,Calcination,Nanostructures
نویسندگان مقاله m جعفر تفرشی | jafar tafreshi
faculty of physics, university of semnan, semnan, iran
سازمان اصلی تایید شده: دانشگاه سمنان (Semnan university)

m فضلی |
faculty of chemistry, university of semnan, semnan, iran
سازمان اصلی تایید شده: دانشگاه سمنان (Semnan university)

z جعفری ایوب | jafari ayoub
faculty of physics, university of semnan, semnan, iran
سازمان اصلی تایید شده: دانشگاه سمنان (Semnan university)

نشانی اینترنتی http://jns.kashanu.ac.ir/article_5417_d04597196df4768870d4ebcfc142189a.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات