عنوان انگلیسی Formation of Poly(vinylidene fluoride) Nanofibers Part II: the elaboration of incompatibility in the electrospinning of its solutions
چکیده انگلیسی مقاله Poly(vinylidene fluoride) (PVDF) fibers with two molecular weights were prepared via electrospinning process. In this process, the concentration of spinning depended drastically on the gelation process. Also, it was experimentally smaller than obtained concentration in the solution entanglement number approach (SENA). Proof of this incompatibility was explained by the properties of PVDF and its solutions with DMF (i.e. PVDF crystallization, microgel formation and spinodal decomposition). These factors caused to early stabilize liquid jet. Also, early gelation inhibited from the fiber formation by blockage of syringe needle with Mw = 180,000 g/mol and early spinodal decomposition helps to fiber formation by isolated droplets of polymer-rich phase with Mw=275,000 g/mol. Finally, a mechanism was proposed for the electrospinning of these solutions.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله a اکبری |
department of carpet, faculty of architecture amp;amp; art, university of kashan, kashan, iran
سازمان اصلی تایید شده: دانشگاه کاشان (Kashan university)

a yunessnia lehi | yunessnia lehi
institute of nanoscience and nanotechnology, university of kashan, kashan, iran
سازمان اصلی تایید شده: دانشگاه کاشان (Kashan university)

نشانی اینترنتی http://jns.kashanu.ac.ir/article_5376_7a2c9a40049c0bdedf12c3ccfb5ff2a3.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات