Journal of Nanostructures، جلد ۱، شماره ۱، صفحات ۷-۱۳
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Chemico- thermal synthesis of nano-structured cobalt with distinct magnetic property
چکیده انگلیسی مقاله The synthesis of nano- structured cobalt through a controlled chemical process followed by heat treating at various temperatures is studied. The product is characterized by ICP, XRD, FESEM , and TEM, indicating that the as- synthesized particles have an amorphous structure with 1.76 for Co/B ratio, an average size of 50 nm. The transformation of intermediate phases into single phase nano- crystalline metallic cobalt during the heat treatment is investigated by DSC analysis. The mean crystallite size of obtained cobalt was 30 nm. The decrease in coercivity (4344.93A/mf) with the sharp increase in saturation magnetization (1.41×10-4 Am2/kg) presents excellent ferro- magnetic properties for nano- crystallite cobalt.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله a عطایی |
school of metallurgy and materials engineering, university of tehran, tehran.
سازمان اصلی تایید شده: دانشگاه تهران (Tehran university)

h sabarou |
school of metallurgy and materials engineering, university of tehran, tehran.
سازمان اصلی تایید شده: دانشگاه تهران (Tehran university)

نشانی اینترنتی http://jns.kashanu.ac.ir/article_5239_60dc152cd0717be5739ec23475b5b0b6.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات