عنوان انگلیسی Synthesis and characterization of high-temperature ceramic YBCO nanostructures prepared from a novel precursor
چکیده انگلیسی مقاله As a new precursor, [tris(2-hydroxyacetophenato) triaqua(III)], [Y(HAP)3(H2O)3]; complex was used in thermal decomposition process for the synthesis of rod-like high-temperature ceramic YBCO with length of about 320-350 nm and diameters 60–90 nm. The as-synthesized products were characterized by XRD, FT-IR, TEM, SEM and EDX analyses. The results showed that by using fine raw materials, the calcination temperature can be reduced to 870 ºC. It was found that this type of precursor have clearly effects on the size and morphology of product because the organic ligands around yttrium center act like a protecting agent to prevent agglomeration.
کلیدواژه‌های انگلیسی مقاله Nanostructure,YBCO,Complex precursor,Thermal decomposition
نویسندگان مقاله m صلواتی نیاسری | salavati niasari
plasma physics research center, science and research, islamic azad university, tehran, iran, institute of nano science and nano technology, university of kashan, kashan, p. o. box. 87317–51167, iran
سازمان اصلی تایید شده: دانشگاه آزاد اسلامی علوم و تحقیقات (Islamic azad university science and research branch)

s علیخان زاد آرانی | alikhanzadeh arani
plasma physics research center, science and research, islamic azad university, tehran, iran
سازمان اصلی تایید شده: دانشگاه آزاد اسلامی علوم و تحقیقات (Islamic azad university science and research branch)

نشانی اینترنتی http://jns.kashanu.ac.ir/article_5246_9c2b822a0904a062da4fd5bd75439146.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات