عنوان انگلیسی Microwave-assisted synthesis of molybdenum oxide nanoparticles
چکیده انگلیسی مقاله This paper focused on a simple approach for synthesis of molybdenum oxide (MoO3) nanoparticles and reports a facile route for synthesis of such nanoparticles, using microwave irradiation as a homogenous and powerful source of heating, using ethylene glycol as the solvent and heating medium. For more investigations, besides microwave heating, the obtained solutions were also treated by conventional heating. Finally, product particles were characterized and compared using scanning electron microscopy (SEM) and energy dispersive x-ray microanalysis (EDX). According to the results, microwave irradiated particles showed a good dispersion and stability in relation to the other sample. So, the obtained product was subjected to X-ray diffraction (XRD) analysis to survey the formation of MoO3 nanoparticles. The transmission electron microscope (TEM) micrographs were also recorded to study the size and morphology of the nanoparticles. According to the results, nanoparticles were spherical with an average size of about 50 nm. The absorbance spectrum of MoO3 nanoparticles was further studied using the UV-spectroscopy and the absorbance peak was observed at 257nm.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله مهرداد manteghain |
tarbiat modares university
سازمان اصلی تایید شده: دانشگاه تربیت مدرس (Tarbiat modares university)

فایزه طاری |
department of engineering, nanomaterial group, tarbiat modares university
سازمان اصلی تایید شده: دانشگاه تربیت مدرس (Tarbiat modares university)

بهروز بزرگی |
department of chemical engineering, tarbiat modares university, tehran, iran.
سازمان اصلی تایید شده: دانشگاه تربیت مدرس (Tarbiat modares university)

نشانی اینترنتی http://jpst.irost.ir/article_118_891c612add22824be9e7bebd23686143.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات