عنوان انگلیسی Estimation of pyrolysis product of LDPE degradation using different process parameters in a stirred reactor
چکیده انگلیسی مقاله Pyrolysis of low density polyethylene (LDPE) by equilibrium fluid catalytic cracking (FCC) was studied in a stirred reactor under different process parameters. In this work, the effect of process parameters such as degradation temperature (420-510°C), catalyst/polymer ratio (0-60%), carrier gas type (H2, N2, ethylene, propylene, Ar and He), residence time and agitator speed (0-300 rpm) on the condensate yield (liquid, gas and coke) and product composition were considered. Reaction products were determined by GC analysis and shown to contain naphthenes (cycloalkanes), paraffins (alkanes), olefins (alkenes) and aromatics. Higher temperature and more catalyst amount enhanced LDPE cracking. The maximum “fuel like” condensed product yield was attained at 450°C and 10% catalyst, respectively and gaseous products increased with increases in temperature. Hydrogen as a reactive carrier gas increased the condensed and paraffinic product yield. Appropriate heat transfer (by stirring) increased the catalyst efficiency in a stirred reactor.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله مهرداد سیفعلی عباس آبادی | seifali abbas abadi
chemical engineering, energy department, kermanshah university of technology, p.o. box 67178-3766, kermanshah, iran|polymerization engineering, iran polymer and petrochemical institute ippi , p.o. box 14965 115, tehran, iran
سازمان اصلی تایید شده: دانشگاه صنعتی کرمانشاه (Kermanshah university of technology)

مهدی نکومنش حقیقی | nekoomanesh haghighi
polymerization engineering, iran polymer and petrochemical institute ippi , p.o. box 14965 115, tehran, iran

armando g مک دوناذ | armando g
department of forest, rangeland and fire sciences, university of idaho, po box 441132, moscow, id 83844-1132, usa

حمید یگانه |
polymerization engineering, iran polymer and petrochemical institute ippi , p.o. box 14965 115, tehran, iran

نشانی اینترنتی http://poj.ippi.ac.ir/article_1102_342.html
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات