عنوان انگلیسی Effect of Welding Parameters in the Microstructure and Mechanical Properties of Friction-Welded Joints of 100Cr6 Steel
چکیده انگلیسی مقاله  In this study, high-carbon, chromium alloy steel (100Cr6) having the initial spheroidized microstructure was welded using the rotary friction welding method. The effects of process parameters such as friction time and friction force were experimentally investigated. The friction welded joints were produced of two 100Cr6 steel rods. In order to examine the microstructure and mechanical properties of the friction welded 100cr6 steel joints, tensile and hardness tests were conducted. The microstructure of weld zone was examined by optical microscopy. It was found that after cooling, martensitic structure is obtained at the core and periphery of the weld joint. It was found that the tensile strength of friction welded samples is increased with increasing time and force of friction up to a certain level and then decreases again. Hardness measurements show a higher hardness at the centre of the weld joint in comparison with its periphery.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله | D. Mourad
Institut d'optique et mecanique de precision -UFA setif - Algerie


| O. El Hedj
Institut d'optique et mecanique de precision -UFA setif - Algerie


| L. Rachid
Institut d'optique et mecanique de precision -UFA setif - Algerie
نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-1988-1&slc_lang=en&sid=1
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/454/article-454-1557044.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات