عنوان انگلیسی CHARACTERIZATION OF HIGH-SILICA MORDENITE OBTAINED BY DIRECT SYNTHESIS
چکیده انگلیسی مقاله Three high-silica mordenite zeolites differing in SiO440, ratio were prepared by direct synthesis without using any template. The products Si02/A120, ratio is influenced by the starting gel composition. This ratio is increased upon ion-exchange with NH,Cl and subsequent calcination to prepare protonic mordenite. The protonic mordenites with Si02/A1203ra tios of 14.6,29.2 and 34.6 were characterized by X-ray diffraction, energy dispersive X-ray microprobe analysis, scanning electron microscopy and thermogravimetric analysis. Catalytic cracking of n-hexane was studied as a measure of catalytic activity of protonic mordenites. Catalytic activities are expressed as conversion percent of n-hexane. Catalysts with higher Si02/A1,03 were found to be more active
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله
نشانی اینترنتی https://jsciences.ut.ac.ir/article_31468_b52852e42743d9b7f886653d167fdaeb.pdf
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/513/article-513-1764289.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات