عنوان انگلیسی Nanoclay‑reinforced polymethylmethacrylate and its mechanical properties
چکیده انگلیسی مقاله Background: Incorporation of extra fillers into dental resins might enhance their physical properties. In this study, the tensile and impact strengths of modified heat‑curing acrylic resin reinforced with nanoclay were investigated. Materials and Methods: In this experimental study, nanoclay-acrylic resin composite was prepared by mixing 0.5, 1, and 2 wt% of nanoclay with methacrylate monomer in an ultrasonic probe, followed by mixing with the polymethylmethacrylate (PMMA) powder. 24 cubic 20 mm × 20 mm × 200‑mm specimens for each test, 18 samples containing nanoclay and 6 samples for the control group and a total of 48 samples were prepared. The tensile and impact strengths of the samples were tested according to ISO 527 and 179, respectively. One‑way ANOVA was used for statistical analysis, followed by multiple comparison tests (Scheffé's test). Statistical significance was set at P < 0.05. Results: The maximum mean tensile and impact strengths were recorded in the control group, and an acrylic resin containing 2% of nanoclay demonstrated the minimum mean in all the tests. Increasing the percentage of nanoclay in PMMA compromised the tensile strength (P < 0.05) with no effect on its impact strength. Conclusion: Incorporation of nanoclay particles into acrylic resins can adversely affect the mechanical properties of the final products, and this effect is directly correlated with the concentration of nanoparticles. Key Words: Impact, nanoparticles, polymethylmethacrylate, strength, tensile strength
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله | Ali Barzegar


| Tahereh Ghaffari


نشانی اینترنتی http://drj.mui.ac.ir/index.php/drj/article/view/1970
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/171/article-171-1956088.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده Original Article(s)
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات