علوم و تکنولوژی پلیمر، جلد ۲۴، شماره ۳، صفحات ۲۳۱-۲۴۰
عنوان فارسی اثر استفاده از نانوخاک رس در الکتروریسی پلی اتاکاپرولاکتون
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Effect of Nanoclay on the Electrospinning of Poly(ε-caprolactone)
چکیده انگلیسی مقاله Nanofber mats of poly(ε-caprolactone)/nanoclay nanocomposites were fabricated by electrospinning. The effects of the solution concentration and the nanoclay content of nanocomposite materials on the fnal nanofber structure were investigated. Morphology and diameter of the nanofbers were studied using optical and scanning electron microscope. It was observed that the poly(ε-caprolactone) at concentration of 5% to 8% could be electrospun into the fbrous structure. The results showed that the presence of the nanoclay promoted the creation of fbrous structures in comparison with the poly(ε-caprolactone) without nanoclay. On the other hand, increasing the nanoclay content resulted in a lower average fber diameter. Shear viscosity and conductivity of the solutions were also reported. The presence of nanoclay increased conductivity and shear viscosity of the solutions. Formation of the nanofbers and decrease in their diameters are discussed on the basis of shear viscosity and conductivity of electrospun solution. This electrospun nanofber could be used for tissue engineering application.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله مهسا رستملو |


مهدی نوری |


جواد مختاری |


نشانی اینترنتی http://jips.ippi.ac.ir/article_593_270.html
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/968/article-968-197282.pdf
کد مقاله (doi)
زبان مقاله منتشر شده fa
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات