علوم و تکنولوژی پلیمر، جلد ۲۳، شماره ۴، صفحات ۲۷۱-۲۸۱
عنوان فارسی بررسی خواص ریزساختاری نانوالیاف موازی پلی آکریلونیتریل جمع آوری شده با استفاده از جریان هوای گرم در روش الکتروریسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Microstructural Characterization of Aligned PAN Nanofibers Collected by Hot Air Flow in Electrospinning Method
چکیده انگلیسی مقاله Amodified technique is designed to prepare aligned nanofibers to challenge the existing limitations in collecting methods of nanofibers such as, thickness of collected layer, alignment and productivity of nanofibers. Collecting and simultaneously heating of the aligned nanofibers were carried out by using a rotating drum fixed on top of syringe needles and applying hot air flow. This electrospinning set up can facilitate heating of the nanofiber in electrospinning zone (distance between two syringe needles).Polyacrylonitrile (PAN) nanofibers were electrospun from its 14 wt% solution in dimethylformamide (DMF) under practical conditions. The above method resulted in low rupture rates and increased maximum take up speedfor two collections. The obtained results from angular power spectrum analysis showed better fiber alignment with increasing take up speed, although SEM studies demonstrated wider diameters of nanofibers being produced bythe modified method. The glass transition temperature (Tg) of all the prepared samples were between 70oC and 90oC. The recorded spectra from FTIR were close to common PAN fibers with peaks at 2240 cm-1 (CN stretch), 2920 cm-1 (CH2 bend), 1450 cm-1 (CH stretch) and 1730 cm-1 (CO stretch) wavenumbers. The diffraction patterns obtained from WAXD techniqueshow also an equatorial peak in 2θ = 17o for PAN nanofibers. Our quantitative analysis of WAXD and FTIR diagrams have revealed positive effects by the modified method on crystallization degree of nanofibers produced athigher take up speeds
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله مهدی صدرجهانی | صدرجهانی


سید عبدالکریم حسینی راوندی | seyed abdolkarim


فرزاد دبیریان |


نشانی اینترنتی http://jips.ippi.ac.ir/article_618_280.html
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/968/article-968-197312.pdf
کد مقاله (doi)
زبان مقاله منتشر شده fa
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات