Journal of Mining and Environment، جلد ۱۰، شماره ۴، صفحات ۱۰۸۳-۱۰۹۳
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Solvent extraction and stripping of zinc from synthetic chloride solution in presence of manganese and cadmium as impurities
چکیده انگلیسی مقاله In this research work, solvent extraction and stripping of zinc ions from a Zn-Mn-Cd-bearing solution was investigated using D2EHPA as the extractant in a chloride medium. The efficiency of the extraction and stripping stages was evaluated separately, and different parameters such as the pH, extractant concentration, reaction temperature, and contact time were studied. Based on the results obtained, 97% of zinc, 14% of manganese, and 3% of cadmium were extracted at pH = 2.5, 10% (v/v) of D2EHPA, and 40 °C from the solution containing 5 g L-1 of each metal ion. The stripping isotherms of zinc, manganese, and cadmium at different pH values showed that manganese and zinc were stripped at two different pH values. Thus more than 70% of manganese and more than 90% of zinc were stripped at pH = 2.5 and pH = 0.5, respectively. Kinetic studies indicated that the extraction and stripping of zinc in the first 0.5-1 minute was high. The McCabe–Thiele diagrams showed that two stages of extraction and two stages of stripping in the continuous counter-current flow condition were adequate to separate zinc from Mn and Cd. The dominant Zn species extracted by D2EHPA was ZnCl+, and the values for the thermodynamic parameters ΔHo, ΔSo, and ΔGo were 25.65 kJ mol−1, 79.20 J K−1 mol−1, and 0.86 kJ mol−1, respectively, which showed that the reaction was endothermic at equilibrium.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله H. Jafari |
School of Mining Engineering, College of Engineering, University of Tehran, Tehran, Iran

H. Abdollahi |
School of Mining Engineering, College of Engineering, University of Tehran, Tehran, Iran

M. Gharabaghi |
School of Mining Engineering, College of Engineering, University of Tehran, Tehran, Iran

A.A. Balesini |
Department of Mechanic and Metallurgy Engineering, Islamic Azad University, Miyaneh Branch, Miyaneh, Iran

نشانی اینترنتی http://jme.shahroodut.ac.ir/article_1569_40fcaf469b683917b3e4cbf83d4ccd22.pdf
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/496/article-496-2053209.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات