عنوان انگلیسی The Ballistic Behavior of High Strength, Low Alloy-100 Steel at Sub-zero Temperatures
چکیده انگلیسی مقاله The ballistic response of the high strength, low alloy (HSLA-100) steel at ambient and temperatures of -400°C, -800°C and -1960°C is investigated in this work. Lambert-jonas equation is used to fit the experimental results into a curve. The effect of quenching on ballistic behavior of HSLA-100 is also studied. The experiments are conducted on 3mm thick rectangular specimens impacted by blunt tip projectiles. The results indicate that for the as-received material, the ballistic limit is nearly the same for ambient and -400°C temperatures, but increases significantly by 30% and 40% for -800°C and -1960°C temperatures, respectively. The same trend is observed for the quenched specimens. However, the increase of ballistic limit is lower for the quenched specimens and is 16% and 30% for -800°C and -1960°C temperatures, respectively. The ballistic test was also simulated using Ls-dyna hydrocode to examine the effect of parameters such as the specimen’s thickness, the projectile’s tip shape and mass on the ballistic limit of the materials.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله S Moradi |
Mechanical Engineering, Buali Sina University of Hamadan

G. H. Majzoubi |
Mechanical Engineering, Buali Sina University of Hamadan

نشانی اینترنتی http://www.ije.ir/article_72849_eda5bb402ca461bdbdd1342de49a853d.pdf
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/409/article-409-2062194.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات