International Journal of Engineering، جلد ۲۹، شماره ۹، صفحات ۱۲۵۷-۱۲۶۲
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Tensile and Physical Properties of Linear Low Density Polyethylene-natural Rubber Composite: Comparison between Size and Filler Types
چکیده انگلیسی مقاله Linear Low Density Polyethylene-Natural Rubber (LLDPE-NR) composites in the ratio of 70:20 were made with different loadings of nanosilica and micro-scale Palm Oil Fuel Ash (POFA). Linear Low Density Polyethylene grafted with maleic anhydride (LLDPE-g-MAH) of 10 wt% was added as a compatibiliser. The composites were produced by using two-roll mill machine. The tensile properties of the composites were determined by carrying out tensile test. From the test, it was found that the tensile strength of LLDPE-NR decreased with increasing weight percentages of POFA in the composition. Tensile strength of LLDPE-NR increased with increasing nanosilica content of the composition. The water absorption test was done on all samples, and it was found that water absorption of LLDPE-NR nanocomposites decreased with increasing nanosilica content. However, water absorption of LLDPE-NR microcomposites increased with increasing POFA content.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله Yanuar Z. Arief |
Institute of High Voltage & High Current, Universiti Teknologi Malaysia

Mohamad Zul Hilmey Makmud |
Physics with Electronics, Universiti Malaysia Sabah

Japar Sahari |
Industrial Chemistry, Universiti Malaysia Sabah

Siti Junian |
Physics with Electronics, Universiti Malaysia Sabah

Mat Uzir Wahit |
Center for Composites, Institute of Vehicle Syste, Universiti Teknologi Malaysia

نشانی اینترنتی http://www.ije.ir/article_72792_533dade3ccdb3410b044591467b8e298.pdf
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/409/article-409-2062245.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات