عنوان انگلیسی Effect of Mo Addition on Nanostructured Ni50Al50 Intermetallic Compound Synthesized by Mechanical Alloying
چکیده انگلیسی مقاله The mechanical alloying process was used to synthesize the Ni50Al50−xMox nanocrystalline intermetallic compound using pure Ni and Al elemental powder. This process was carried out in the presence of various Mo contents as a micro-alloying element for various milling times. Structural changes of powder particles during mechanical alloying were studied by X-ray diffractometry (XRD) and scanning electron microscopy (SEM). Results showed that mechanical alloying in various combinations was completed after 48 h of milling time. Minimum crystallite size of the as-milled powders (∼10 nm) was achieved after introducing Mo and milling for 128 h. Also, lattice strain decreased with increasing milling time up to 48 h and again increased after 48 h of milling time. On the other hand, the presence of Mo significantly affected variation intensity of the lattice parameter and morphology of the powder particles.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله gholamhosein akbari |
metallorgy, shahid bahonar kerman

Ali khajesarvi |
Materials Science and Engineering, shahid bahonar kerman

نشانی اینترنتی http://www.ije.ir/article_72582_4a208957356094d91ad2b52e905e1fcd.pdf
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/409/article-409-2062453.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات