عنوان انگلیسی Applications of Impedance Plane and Magnetic Differential Permeability in Microstructural Characterization of AISI D2 Tool Steel
چکیده انگلیسی مقاله Two nondestructive electromagnetic/magnetic techniques including hysteresis loop and eddy current methodologies have been used to characterize microstructural changes of AISI D2 cold work tool steel as a result of quench and tempering treatments. To measure the fraction retained austenite in quenched microstructure, six specimens were austenitized in the range of 1000-1130 °C. Samples austenitized at 1080 °C were also tempered in the range of 200-650 °C for characterization by eddy current and magnetic hysteresis loop outputs, nondestructively. Impedance point movement and maximum differential permeability were measured as a function of austenitizing/tempering temperature to characterize the microstructural features. The study shows that there are good correlations between microstructural variations detected by destructive methods (hardness, XRD and microscopic observation) and outputs of the nondestructive techniques.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله Mehrdad Kashefi |
Materials and Metallurgical Engineering, Ferdowsi University of Mashhad

Saeed Kahrobaee |
Materials and Metallurgical Engineering, Ferdowsi University of Mashad

نشانی اینترنتی http://www.ije.ir/article_72449_6938c5c2b1e9c107f0a966e20b7a49a3.pdf
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/409/article-409-2062582.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات